From: High strength and ductility in partially recrystallized Fe₄₀Mn₂₀Cr₂₀Ni₂₀ high-entropy alloys at cryogenic temperature

High strength and ductility in partially recrystallized Fe<sub>40</sub>Mn<sub>20</sub>Cr<sub>20</sub>Ni<sub>20</sub> high-entropy alloys at cryogenic temperature

Figure 6. TEM micrograph of Fe₄₀Mn₂₀Cr₂₀Ni₂₀ HEA. (A) Bright-field TEM images for HEA. (B-D) TEM images of a precipitate and twins in a tensile specimen strained to fracture at 77 K. (E) SAED patterns indexed as a tetragonal-structured precipitate along the zone direction of [101]. (F) SAED pattern of the twin in (D). TEM: Transmission electron microscopy; HEA: high-entropy alloy; SAED: selective area electron diffraction.