From:  The effect of chromium content on the corrosion behavior of ultrafine-grained CrxMnFeCoNi high-entropy alloys in sulfuric acid solution
The effect of chromium content on the corrosion behavior of ultrafine-grained Cr<i><sub>x</sub></i>MnFeCoNi high-entropy alloys in sulfuric acid solution

Figure 3. EBSD IPF maps and the average grain size distribution of the as-sintered CrxMnFeCoNi (x = 0, 0.6, 1, and 1.5) HEAs. (A) Cr0, (B) Cr0.6, (C) Cr1 and (D) Cr1.5. EBSD: Electron backscatter diffraction; IPF: inverse pole figure; HEAs: high-entropy alloys.

Microstructures
ISSN 2770-2995 (Online)
Navigation
Follow Us
Navigation

Committee on Publication Ethics

https://publicationethics.org/members/microstructures

Portico

All published articles are preserved here permanently:

https://www.portico.org/publishers/oae/

Committee on Publication Ethics

https://publicationethics.org/members/microstructures

Portico

All published articles are preserved here permanently:

https://www.portico.org/publishers/oae/
partners@oaepublish.com Company Contact Us
Discover Content
Follow OAE
Twitter
Facebook
LinkedIn
YouTube
BiLiBiLi
WeChat
© 2016-2024 OAE Publishing Inc., except certain content provided by third parties