What lies beneath? Investigations of atomic force microscopy-based nano-machining to reveal sub-surface ferroelectric domain configurations in ultrathin films
0
, ... Abstract
Multiferroic materials, encompassing simultaneous ferroelectric and ferromagnetic polarization states, are enticing multi-state materials for memory scaling beyond existing technologies. Aurivillius phase B6TFMO
Keywords
INTRODUCTION
As miniaturization of electronic devices continues, a key condition for materials in memory storage technologies is the extension of their functional properties to ultrathin (sub-10 nm) thicknesses. This is challenging for multiferroics and ferroelectrics, given that ferroelectricity is a collective effect between competing short-range covalent repulsions and long-range Coulomb interactions. These interactions will alter as the collective distortion of unit cells (u.c.) within the lattice is adjusted on decreased thickness, and the spontaneous ferroelectric polarization is projected only to be supported above a particular critical thickness[1]. A consequence of fabricating low-dimensional ferroelectric nanostructures is an increase in surface area, which can result in enlarged depolarization field strengths (of magnitude inversely proportional to the thickness of the ferroelectric) if the surface charges are not completely screened. Below the critical thickness, out-of-plane ferroelectricity is destabilized, tending to a decline in performance and a lack of reproducibility. In 1997, this critical thickness was thought to be 20 nm[2]; however, considerable advancements in thin film synthesis and characterization over the last two decades[3] have enabled demonstration of stable out-of-plane ferroelectricity in high-quality ultrathin films at dimensions much thinner than this. Exploitation of epitaxial strain and confinement strain, along with effective screening of interface and surface charges, can counteract the opposing effects of thickness reduction and stabilize out-of-plane ferroelectricity at reduced dimensions. Out-of-plane ferroelectricity has been measured at a minimum thickness of 4 nm (10 u.c.) for Pb(Zr0.2Ti0.8)O3[4], 1.2 nm (3 u.c.) for PbTiO3[5], 1 nm for BaTiO3[6], and 1 nm (2 u.c.) for Hf0.8Zr0.2O2[7].
Moreover, the problems pertaining to depolarization field effects are substantially diminished for in-plane polarization directions. Polarization is lateral to the surface for all in-plane directions and is, therefore, not impeded by contesting depolarization fields upon scaling down to ultrathin thicknesses[8]. A family of materials possessing large in-plane spontaneous polarizations [Ps (≈ 0.4 C m-2)] are the Aurivillius phase materials described by the general formula Bi2O2(Am1BmO3m+1))[9-14]. They are a well-established group of ferroelectrics and a technologically important class of material. SrBi2Ta2O9 (m = 2) and Bi3.25La0.75Ti3O12
Figure 1. (A) Schematic of an m = 5 Aurivillius phase crystal structure (space group B2eb) projected down the <110> orientation[43,59]. Half a u.c. (c/2) consists of five perovskite blocks between fluorite-type bismuth oxide layers. (B) Representative XRD patterns of
It is widely acknowledged[31,32] that a ferroelectric domain structure is the initial governing factor in polarization switching behavior, influencing domain wall motion, evolution of existing ferroelectric domains, and the nucleation and development of further ferroelectric domains. The equilibrium domain configuration in a ferroelectric thin film arises from the minimization of the elastic and electrostatic energies in the crystal and is influenced by factors such as the film composition, growth mechanism, growth and cooling temperatures, underlying substrate, electrodes, and thin film thickness. Therefore, the characterization, understanding, and tailoring of ferroelectric domain structures in ultrathin films is imperative for controlling electromechanical properties and device applications. Piezoresponse force microscopy (PFM) is a powerful tool for probing ferroelectric phenomena at nanoscale and can reveal fundamental information on domain size, orientation, pattern, anisotropy/isotropy, and the nature of the domain walls that separate the ferroelectric domains. PFM experiments demonstrate that stable and switchable ferroelectricity persists in sub-8 nm Aurivillius B6TFMO films, initiating options for miniaturizing innovative multiferroic-based devices incorporating ultrathin tunnel junctions[27,28]. However, because B6TFMO thin film synthesis tends to proceed by a 2D nucleation and layer-by-layer growth mechanism[33], it can be difficult to control the formation of intermediary steps in the layer-by-layer growth mode, particularly at sub-10 nm film thickness. As a result, incomplete growth layers corresponding to heights of half of a unit cell of the Aurivillius phase (~2.5 nm thick) are visible on the film surface, complicating the surface PFM images and obscuring the ferroelectric domain configuration of the underlying B6TFMO film[24,27].
In recent years, AFM tip-based nano-machining has been recognized as an emerging technology for machining nanostructures, nanometer-scale 3D imaging of material properties and photomask repair[34-39]. In this contribution, we employ a commercially available probe to perform atomic force microscopy (AFM)-based nano-machining to remove surface artifacts and expose the underlying ferroelectric domain configuration of 7.9 nm (1.5 u.c.) and 5.6 nm (1 u.c.) B6TFMO films. We perform PFM investigations as a function of milled depth (from surface to substrate) to investigate domain structures and persistence of ferroelectricity through the ultrathin B6TFMO films.
MATERIALS AND METHODS
Ultrathin film synthesis
B6TFMO thin films were fabricated using a horizontal flow AIXTRON AIX 200/4FE AVD direct liquid injection chemical vapor deposition (DLI-CVD) system using processes similar to those previously described by Keeney et al.[27,28], Bismuth, iron, and titanium precursor solutions [0.1 mol dm-3 solutions of Bi(thd)3, Fe(thd)3, and Ti(O-iPr)2(thd)2 (where thd = 2,2,6,6-tetramethyl 3,5-heptanedionate;
Physical characterization
The crystallographic structure of the films was determined using a Panalytical MRD X-Pert Pro X-ray diffraction (XRD) system with a filtered Cu K radiation source (λ = 0.1541876 nm). The setup included a vertical magnetic strip mount, a 2 mm mask, and a divergence slit of 0.5°. Scans were conducted over a 2θ
AFM-based nano-machining and PFM experiments
AFM-based nano-machining of the surfaces of the ultrathin B6TFMO films was achieved using an Asylum Research MFP-3DTM AFM by applying force from a sufficiently stiff diamond cantilever. NM-RC (single crystal diamond, Au reflex coated, < 10 nm tip radius, 486 kHz resonant frequency, boron-doped) probes, commercially available from Adama Innovations (c/o Republic of Work, 12 South Mall, Cork, T12 RD43, Ireland), were used for the AFM-based nano-machining studies. The normal loading force, F (N), was calculated using Hookes law, F = kz, where k is the spring constant (N/m), and z (m) is determined by multiplying the calibrated deflection sensitivity (m/V) by the setpoint (V) (the difference between photodiode signal when the cantilever is far from the surface and when it is at setpoint). The spring constant [1.89 × 102 (±8.39%) N/m] was calibrated via the Sader method[41] by performing a thermal tune (1,000 samples) in free air to measure the resonance frequency and the quality factor of the cantilever. Loading forces of between 1.86 µN and 5.59 µN were utilized for each scan in this work. Successive scans were performed over 8 µm × 8 µm areas at a scan frequency of 0.75 Hz to progressively machine through the sample from the film surface until the substrate was reached. A machining scan angle of 90° was utilized unless otherwise specified. The depths of the nano-machined areas were measured by performing line section height profiles of imaged areas. The measured RMS roughness values for the nano-machined areas of the 7.9 nm B6TFMO sample were, in general, rougher [values of 0.52 nm (SD = ±0.42 nm), 0.46 nm
RESULTS AND DISCUSSION
Characterization of structure, surface morphology, and surface piezo-configurations of as-prepared ultrathin B6TFMO films
Two different thicknesses of B6TFMO films were synthesized on (001)-orientated NGO substrates by pulsing either 75 injections or 100 injections of each precursor during the DLI-CVD process. The pseudo-cubic lattice parameter (ap′) of the perovskite-type layer in B6TFMO is 3.89 Å and ap′ is 3.858 Å for NGO; therefore, the lattice mismatch = -0.82%[27]. Out-of-plane XRD profiles, as shown in Figure 1B, are consistent with epitaxial films of an orthorhombic Aurivillius phase with five perovskite layers per half unit cell (m = 5) interleaved by bismuth oxide interfaces, as depicted schematically in Figure 1A[43]. Both B6TFMO films demonstrate a preference for orientating along the c-axis of the structure, with only (00l) Bragg reflections visible in the diffractograms. The broadening of the peaks [e.g., FWHM values for the (0010), (0012), and (0020) peaks are 1.721°, 0.400°, and 2.114° and are 1.534°, 0.389° and 1.186° for B6TFMO deposited with 75 injections and 100 injections, respectively] is due to grain size effects and due to the fact that the X-ray beam is scattering from only three, or less, half-unit cell repeat entities[44]. Comparative XRD patterns obtained from B6TFMO films deposited with 75 injections and 100 injections demonstrate that the intensities of the film deposited using 75 injections [e.g., the log10 intensity of the (0010), (0012), and (0020) peaks are: 0.461, 0.616, and 0.130 counts] are lower than the intensities of the film deposited using 100 injections [e.g., the log10 intensity of the (0010), (0012), and (0020) peaks are: 0.717, 0.951, and 0.371 counts], corresponding to a decreased film thickness for the film deposited using 75 injections. HR-TEM imaging
Epitaxial growth of layered Aurivillius phases under high supersaturation conditions is inclined to proceed via a 2D nucleation and layer-by-layer (Frank-Van der Merwe) growth mode[27-30,33,45], as illustrated in Figure 2A. Laterally grown layers with heights consistent with the lattice parameter of half of a u.c. of the Aurivillius structure evolve and increasingly merge and condense to form a complete (flat) layer prior to the nucleation of subsequent half-unit cell-thick layers. Each complete growth layer is ~2.5 nm in thickness for B6TFMO. Depending on the level of saturation during intermediary steps in the layer-by-layer growth mode, either 2D islands or pits (holes) can be seen on the film surface. The pits are referred to as “loch-keime” (hole-nuclei), which are “negative” 2D islands[33]. These types of 2D islands and pits are visible in the HR-TEM images in Figure 2B and the AFM image in Figure 2C for the 7.9 nm (1.5 u.c.) and 5.6 (1 u.c.) nm B6TFMO films. The coalescence of the laterally grown layers can be seen in Figure 2C, where the majority of the incomplete surface is covered by the growing 2-D layer, with darker regions in between corresponding to the underlying layer beneath (“negative” 2D islands). The height (depth) of these Aurivillius phase 2D islands (pits) is approximately 2.5 nm, corresponding to half a unit cell (c/2) of the
Figure 2. (A) A schematic of the 2D nucleation and layer-by-layer (Frank-Van der Merwe) growth mode. (B) Representative HR-TEM images demonstrating the presence of 2D islands and pits in the 7.9 nm thick B6TFMO film on NGO (001). (C) Representative AFM image of 5.6 nm thick B6TFMO film NGO (001) substrates. A line section profile 1 is shown in white through the 2D pits indicating a height of 2.5 nm, corresponding to half a u.c. (c/2) of the m = 5 Aurivillius structure (see Figure 1A). Small circular island-type inclusions (< 20 nm diameter) are encircled in red. (D) Lateral (Lat) PFM Amp and Phase images of the pristine surface of a 7.9 nm thick B6TFMO film.
DART-PFM imaging [Figure 2D] and [Supplementary Figure 1] utilizing a conducting diamond probe with an apex super sharp tip (radius < 5 nm) demonstrates that a random mixture of piezoresponse with indiscriminate orientation is exhibited for measurements of the pristine surface of the 7.9 nm (1.5 u.c.) thick B6TFMO film. 180 phase contrast is displayed for oppositely polarized domains, separated by curved domain walls. Lateral PFM imaging [Figure 2D] and [Supplementary Figure 1A-C] enables measurement of the in-plane polarization components[42], whereas vertical PFM images [Supplementary Figure 1D and E] provide information on the out-of-plane component. Average surface in-plane domain sizes of 440 nm2
Investigations of ferroelectric domain configuration in ultrathin B6TFMO as a function of AFM-based nano-machined depth
Progress in the miniaturization of semi-conductor processes has created an increased demand for AFM-based nanomachining to satisfy the role of defect removal with nano-meter level accuracy during photomask repair[37-39]. In this work, we apply the AFM-based nano-machining approach to remove surface contaminants from the ultra-thin B6TFMO films to uncover a complete Aurivillius phase surface layer. Successive scanning allows progressive nano-machining of the film at increased depths with nanometer-level control. A sufficiently stiff, commercially available diamond probe was used with a removal rate of between 0.13 nm/scan and 0.41 nm/scan.
Next, we performed PFM imaging of the 7.9 nm (1.5 u.c.) B6TFMO film as a function of nano-machined thickness. Lateral PFM results, scanned with the long-axis of the cantilever orientated parallel to the NGO [010] direction, are shown in Figure 3. While a randomly distributed piezoresponse without a favored domain orientation is observed for the pristine film surface [Figure 3A-C], on removal of 0.7 nm of the film surface [Figure 3D-F], it is revealed that spontaneous polarization orientates in distinct stripe domain configurations along the a-b plane, at 45° to the orthorhombic b-axis of NGO. Vertical PFM images
Figure 3. Representative topography and lateral (lat) DART-PFM phase and amplitude (amp) images of 7.9 nm (1.5 u.c.) B6TFMO on NGO (001) as a function of AFM-based nano-machined depth. The scanning direction of the cantilever was parallel with the
Gradauskaite et al.[29,30] and Keeney et al.[27] previously observed stripe domains for one u.c. thick (5 nm) Aurivillius phase films that were terminated with complete Aurivillius layers and exhibited an atomically flat surface. It was deemed that domain patterns are stabilized by the underlying NGO substrate, where the lattice mismatch is progressively lost as film thickness increases. For films of two unit cells in thickness, an isotropic random distribution of 180° domains was observed[29,30]. Therefore, the question arises as to whether the onset of 45° striped domain observation in this work happens solely due to the ability to image the B6TFMO film at decreased thickness, where the domain patterns are possibly stabilized by substrate strain effects. Alternatively, the onset of striped domain observation from the nano-machining process may be due to the removal of otherwise masking surface 2D islands, pits, and contaminants to reveal a smooth B6TFMO surface terminated with a complete Aurivillius layer.
To distinguish between the two possibilities, PFM imaging was performed on the thinner 5.6 nm (1 u.c.) B6TFMO film, prepared by the same layer-by-layer growth process as the 7.9 nm (1.5 u.c.) thick B6TFMO film. Lateral DART-PFM images, scanned with the long-axis of the cantilever orientated parallel to the NGO [100] direction, are shown in Figure 4. Based on the results of the 7.9 nm (1.5 u.c.) thick B6TFMO films in Figure 3G-I, where the milled depth corresponds to a thickness of 5.9 nm and results from previous 5 nm-thick B6TFMO films exhibiting an atomically flat surface[27], we would expect to see 45° striped domain patterns for the 5.6 nm (1 u.c.) B6TFMO film. However, a random mixture of piezoresponse with indiscriminate orientation is exhibited for measurements of the pristine surface of the 5.6 nm (1 u.c.) thick B6TFMO film, as shown in Figure 4A-C. 180 degree phase contrast is displayed for oppositely polarized domains with average surface in-plane domain sizes of 209 nm2 (SD = 274 nm2). Therefore, the observation of the randomly distributed piezoresponse in this work is due to the surface 2D islands, pits, and contaminants complicating the surface PFM signal. Stripe domain configurations along the a-b plane, at 45° to b-axis of the orthorhombic unit cell of NGO, are uncovered by PFM imaging on removal of surface contaminants by nanomachining at depths of 0.4 nm [Figure 4D-F], 3.7 nm [Figure 4G-I], 4.6 nm
Figure 4. Representative topography and lateral (lat) DART-PFM phase and amplitude (amp) images of 5.6 nm (1 u.c.) B6TFMO on NGO (001) as a function of AFM-based nano-machined depth. The scanning direction of the cantilever scanning direction was parallel with the [100]substrate axis.
The measured domain widths are of the order of 0.08 µm for the nano-machined 5.6 nm (1 u.c.) B6TFMO sample; narrower than that observed for the thicker 7.9 nm (1.5 u.c.) B6TFMO sample, consistent with the Landau-Lifshitz-Kittel scaling law[48-50]. In the PFM images, striped domains are directed from the top left to the bottom right in the 7.9 nm (1.5 u.c.) B6TFMO sample where the PFM cantilever was aligned parallel to the [010] substrate direction, whereas domains are directed from top right to bottom left in the 5.6 nm
Crystal symmetry of the Aurivillius phases dictates that the major in-plane spontaneous polarization component lies entirely along the a axis (with a minor polarization along the out-of-plane c-axis in odd-layered structures)[43]. Therefore, there must be another physical origination for the experimentally observed 45° striped domains. a-b crystal twinning is a common occurrence in layered materials such as the layered high temperature superconductors[53] and Aurivillius phases[54]. The lack of uniaxial polarization in this work indicates that crystal twinning is present in the B6TFMO thin films. The crystal twinning would originate from the orthorhombic crystal structure of the underlying (001) NGO substrate, which presents an anisotropic template for growth based on a pseudo-cubic unit cell[53]. The a axis of the pseudo-cubic cell lies along the ab diagonals of the orthorhombic NGO crystal structure, and a pseudo-cubic lattice constant of 3.858 Å is presented for NGO. This provides a close lattice match to the ap’ of B6TFMO (3.89 Å) to grow under minimal strain[27]; however, the angular anisotropy of the pseudo-cubic template would likely give rise to preferential twinning. The experimental observations of 45 orientated stripe domains, rather than expected in-plane uniaxial anisotropy, may be the result of crystal twinning in B6TFMO created by mimicking the pseudo-cubic symmetry of the underlying NGO substrate.
CONCLUSIONS
In summary, we demonstrate the use of AFM-based nano-machining using a commercially available diamond probe to remove surface contaminants from ultrathin B6TFMO films with nanometer-level precision. Complete Aurivillius layers are uncovered beneath the as-grown surface, with subsequent lateral PFM imaging revealing distinct stripe domain configurations along the a-b plane (at 45° to the NGO substrate b-axis), of stark contrast to the randomly distributed piezoresponse observed for the pristine film surface. We attribute the differences in piezo-configuration between the pristine surface and exposed sub-surfaces to the effectiveness of AFM-based nano-machining in removing growth surface artifacts (fractional Aurivillius phase 2D islands/pits and secondary phase contaminants) that, otherwise, mask the domain configurations of the underlying planar B6TFMO film. The experimental observations of 45° orientated stripe domains rather than in-plane uniaxial anisotropy are likely ensuing from the presence of crystal twinning in B6TFMO to conform to the pseudo-cubic symmetry of the underlying NGO substrate. The width of the 45° stripe domains is narrower for the 5.6 nm B6TFMO films (0.08 µm) compared to the 7.9 nm B6TFMO films (0.14 µm), consistent with the Landau-Lifshitz-Kittel scaling law[48-50]. Moreover, while previous PFM investigations of multiferroic m = 5 B6TFMO films demonstrated the persistence of stable ferroelectricity close to the unit cell level (5 nm to 8 nm)[27,28], the AFM-based nano-machining investigations in this work indicate that ferroelectricity persists at thicknesses lower than this. Stable sub-surface ferroelectric domain structures and piezoresponses persist along the in-plane directions throughout the film depth, down to less than half of an Aurivillius phase unit cell (< 2.5 nm). These findings, along with evidence for sub-unit cell ferroelectricity in exfoliated flakes[26] and planar thin films[29] of m = 4 Aurivillius phases, demonstrate the technological potential of Aurivillius phase B6TFMO for future miniaturized memory storage devices. For example, devices based on in-plane tunnel junctions are an appealing prospect, as they would not be expected to be obstructed by opposing depolarization fields upon thickness-scaling to ultrathin dimensions. This means that higher tunnelling current ratios could be achieved with non-destructive read processes. To date, no such in-plane devices have been commercialized; only theoretical device models based on monochalcogenides have been reported. However, it is difficult to synthesize high-quality ultra-thin monochalcogenides by scalable growth methods[55-58]. As such, optimized multiferroic B6TFMO Aurivillius phases, which can be synthesized by scalable DLI-CVD growth methods, are perfect candidates for utilization in next-generation devices based on ultrathin multiferroic tunnel junctions.
DECLARATIONS
Acknowledgments
The authors gratefully acknowledge the support of the Royal Society-Science Foundation Ireland (SFI) University Research Fellowship URF\R\201008 and the SFI Frontiers for the Future Project 19/FFP/6475.
Authors’ contributions
Conceiving and coordinating the project, developing the DLI-CVD processes, synthesizing the ultra-thin B6TFMO thin films, and performing AFM and PFM characterization and AFM-based nanomachining experiments; interpreting the results in discussion with the other authors; initially writing of the first draft of the manuscript, with the final version being crafted through contributions from all authors: Keeney L
Making substantial contributions to the conception and design of the AFM-based nanomachining studies: Colfer L
Performing XRD characterization and interpreting the ultrathin B6TFMO films: Dutta D
Conducting FIB cross-sectioning of lamellae for TEM and performing HR-TEM analysis of the B6TFMO thin films: Schmidt M
Handling XRR analysis and interpretating the ultrathin B6TFMO films: Wei G
All authors have given their approval to the final version of the manuscript.
Availability of data and materials
The accepted publication is available on the open access University College Cork (UCC) CORA repository
Financial support and sponsorship
This work was supported by the Royal Society-Science Foundation Ireland (SFI) University Research Fellowship URF\R\201008 and the SFI Frontiers for the Future Project 19/FFP/6475.
Conflicts of interest
All authors declared that there are no conflicts of interest.
Ethical approval and consent to participate
Not applicable.
Consent for publication
Not applicable.
Copyright
© The Author(s) 2023.
Supplementary Materials
REFERENCES
2. Li S, Eastman JA, Vetrone JM, Foster CM, Newnham RE, Cross LE. Dimension and size effects in ferroelectrics. Jpn J Appl Phys 1997;36:5169.
3. Qiao H, Wang C, Choi WS, Park MH, Kim Y. Ultra-thin ferroelectrics. Mater Sci Eng R Rep 2021;145:100622.
4. Tybell T, Ahn CH, Triscone J. Ferroelectricity in thin perovskite films. Appl Phys Lett 1999;75:856-8.
5. Fong DD, Stephenson GB, Streiffer SK, et al. Ferroelectricity in ultrathin perovskite films. Science 2004;304:1650-3.
6. Choi KJ, Biegalski M, Li YL, et al. Enhancement of ferroelectricity in strained BaTiO3 thin films. Science 2004;306:1005-9.
7. Cheema SS, Kwon D, Shanker N, et al. Enhanced ferroelectricity in ultrathin films grown directly on silicon. Nature 2020;580:478-82.
8. Vasudevan RK, Matsumoto Y, Cheng X, et al. Deterministic arbitrary switching of polarization in a ferroelectric thin film. Nat Commun 2014;5:4971.
9. Guo YY, Gibbs AS, Perez-Mato JM, Lightfoot P. Unexpected phase transition sequence in the ferroelectric Bi4Ti3O12. IUCrJ 2019;6:438-46.
10. Deepak N, Zhang PF, Keeney L, Pemble ME, Whatmore RW. Atomic vapor deposition of bismuth titanate thin films. J Appl Phys 2013;113:187207.
11. Keeney L, Groh C, Kulkarni S, Roy S, Pemble ME, Whatmore RW. Room temperature electromechanical and magnetic investigations of ferroelectric Aurivillius phase Bi5Ti3(FexMn1-x)O15 (x = 1 and 0.7) chemical solution deposited thin films. J Appl Phys 2012;112:024101.
12. Keeney L, Kulkarni S, Deepak N, et al. Room temperature ferroelectric and magnetic investigations and detailed phase analysis of Aurivillius phase Bi5Ti3Fe0.7Co0.3O15 thin films. J Appl Phys 2012;112:052010.
13. Keeney L, Zhang PF, Groh C, Pemble ME, Whatmore RW. Piezoresponse force microscopy investigations of Aurivillius phase thin films. J Appl Phys 2010;108:042004.
14. Zhang PF, Deepak N, Keeney L, Pemble ME, Whatmore RW. The structural and piezoresponse properties of c-axis-oriented Aurivillius phase Bi5Ti3FeO15 thin films deposited by atomic vapor deposition. Appl Phys Lett 2012;101:112903.
15. Wouters DJ, Maes D, Goux L, et al. Integration of SrBi2Ta2O9 thin films for high density ferroelectric random access memory. J Appl Phys 2006;100:051603.
16. Park BH, Kang BS, Bu SD, Noh TW, Lee J, Jo W. Lanthanum-substituted bismuth titanate for use in non-volatile memories. Nature 1999;401:682-4.
17. Annual report pursuant to section 13 or 15(d) of the securities exchange act of 1934 for the fiscal year ended March 31, 2006 commission file number 1 - 6784. Available from: https://www.sec.gov/Archives/edgar/data/63271/000119312506188347/d20f.htm [Last accessed on 16 Oct 2023].
18. Fujii E, Uchiyama K. First 0.18 μm SBT-based embedded FeRAM technology with hydrogen damage free stacked cell structure. Integr Ferroelectr 2003;53:317-23.
19. Pitcher MJ, Mandal P, Dyer MS, et al. Magnetic materials. Tilt engineering of spontaneous polarization and magnetization above
20. Suwardi A, Prasad B, Lee S, et al. Turning antiferromagnetic Sm0.34Sr0.66MnO3 into a 140 K ferromagnet using a nanocomposite strain tuning approach. Nanoscale 2016;8:8083-90.
21. Choi EM, Maity T, Kursumovic A, et al. Nanoengineering room temperature ferroelectricity into orthorhombic SmMnO3 films. Nat Commun 2020;11:2207.
22. Srihari NV, Vinayakumar KB, Nagaraja KK. Magnetoelectric coupling in bismuth ferrite - challenges and perspectives. Coatings 2020;10:1221.
23. Keeney L, Maity T, Schmidt M, et al. Magnetic field-induced ferroelectric switching in multiferroic aurivillius phase thin films at room temperature. J Am Ceram Soc 2013;96:2339-57.
24. Faraz A, Maity T, Schmidt M, et al. Direct visualization of magnetic-field-induced magnetoelectric switching in multiferroic aurivillius phase thin films. J Am Ceram Soc 2017;100:975-87.
25. Moore K, O'Connell EN, Griffin SM, et al. Charged domain wall and polar vortex topologies in a room-temperature magnetoelectric multiferroic thin film. ACS Appl Mater Interfaces 2022;14:5525-36.
26. Keeney L, Smith RJ, Palizdar M, et al. Ferroelectric behavior in exfoliated 2D aurivillius oxide flakes of sub-unit cell thickness. Adv Elect Materials 2020;6:1901264.
27. Keeney L, Saghi Z, O’sullivan M, Alaria J, Schmidt M, Colfer L. Persistence of ferroelectricity close to unit-cell thickness in structurally disordered aurivillius phases. Chem Mater 2020;32:10511-23.
28. Keeney L, Colfer L, Schmidt M. Probing ferroelectric behavior in sub-10 nm bismuth-rich aurivillius films by piezoresponse force microscopy. Microsc Microanal 2022;28:1396-406.
29. Gradauskaite E, Campanini M, Biswas B, et al. Robust in-plane ferroelectricity in ultrathin epitaxial aurivillius films. Adv Materials Inter 2020;7:2000202.
30. Gradauskaite E, Gray N, Campanini M, Rossell MD, Trassin M. Nanoscale design of high-quality epitaxial aurivillius thin films. Chem Mater 2021;33:9439-46.
31. Wang Y, Chen W, Wang B, Zheng Y. Ultrathin ferroelectric films: growth, characterization, physics and applications. Materials 2014;7:6377-485.
32. Lines ME, Glass AM. Principles and applications of ferroelectrics and related materials. Oxford: Oxford University Press; 1977. p.525. Available from: https://academic.oup.com/book/25990 [Last accessed on 11 Oct 2023].
33. Venables JA, Spiller GDT, Hanbucken M. Nucleation and growth of thin films. Rep Prog Phys 1984;47:399.
35. Steffes JJ, Ristau RA, Ramesh R, Huey BD. Thickness scaling of ferroelectricity in BiFeO3 by tomographic atomic force microscopy. Proc Natl Acad Sci USA 2019;116:2413-8.
36. Wang J, Yan Y, Li Z, Geng Y, Luo X, Fan P. Processing outcomes of atomic force microscope tip-based nanomilling with different trajectories on single-crystal silicon. Precis Eng 2021;72:480-90.
37. Iwata F, Saigo K, Asao T, et al. Removal method of nano-cut debris for photomask repair using an atomic force microscopy system. Jpn J Appl Phys 2009;48:08JB20.
38. Robinson T, Dinsdale A, Bozak R, White R, Archuletta M. Nanomachining processes for 45, 32 nm mode mask repair and beyond. Procedings of the Photomask and Next-Generation Lithography Mask Technology XV; 2008 May 19; Yokohama, Japan.
39. Robinson T, Dinsdale A, Bozak R, Arruza B. Advanced mask particle cleaning solutions. Procedings of the SPIE Photomask Technology; 2007 Oct 30; Monterey, United States.
40. Bartkowska JA, Bochenek D, Niemiec P. Multiferroic aurivillius-type Bi6Fe2-xMnxTi3O18 (0 ≤ x ≤ 1.5) ceramics with negative dielectric constant. Appl Phys A 2018;124:823.
41. Sader JE, Borgani R, Gibson CT, et al. A virtual instrument to standardise the calibration of atomic force microscope cantilevers. Rev Sci Instrum 2016;87:093711.
42. Kalinin SV, Rodriguez BJ, Jesse S, et al. Vector piezoresponse force microscopy. Microsc Microanal 2006;12:206-20.
43. Ismunandar, Kamiyama T, Hoshikawa A, et al. Structural studies of five layer Aurivillius oxides: A2Bi4Ti5O18 (A = Ca, Sr, Ba and Pb). J Solid State Chem 2004;177:4188-96.
44. Holder CF, Schaak RE. Tutorial on powder X-ray diffraction for characterizing nanoscale materials. ACS Nano 2019;13:7359-65.
45. Frank FC, van der Merwe JH. One-dimensional dislocations III. Influence of the second harmonic term in the potential representation, on the properties of the model. Proceedings of the Royal Society of London; 1949 Dec 22; London, UK. London: Royal; pp. 125-34.
46. Trolier-mckinstry S. Crystal chemistry of piezoelectric materials. In: Safari A, Akdoğan EK, editors. Piezoelectric and acoustic materials for transducer applications. Boston: Springer US; 2008. pp. 39-56.
47. Whatmore, R. Ferroelectric materials. In: Kasap S, Capper P, editors. Springer handbook of electronic and photonic materials. Springer International Publishing: Cham; 2017. p. 1.
48. Landau L, Lifshitz E. 3 - on the theory of the dispersion of magnetic permeability in ferromagnetic bodies. In: Pitaevski LP editors. Perspectives in theoretical physics. The collected papers of E. M. Lifshitz. Amsterdam:Elsevier; 1992. pp. 51-65.
49. Kittel C. Theory of the structure of ferromagnetic domains in films and small particles. Phys Rev 1946;70:965.
51. Wang H, Liu ZR, Yoong HY, et al. Direct observation of room-temperature out-of-plane ferroelectricity and tunneling electroresistance at the two-dimensional limit. Nat Commun 2018;9:3319.
52. Gradauskaite E, Meier QN, Gray N, et al. Defeating depolarizing fields with artificial flux closure in ultrathin ferroelectrics. arXiv 2022:2212;11073.
53. Nam J, Hughes RA, Castellan JP, Gaulin BD, Britten JF, Preston JS. The origin of preferential twinning in YBa2Cu3O7-δ thin films deposited on the (0 0 1) NdGaO3 substrate. J Appl Phys 2005;97:123906.
54. Zurbuchen MA, Cahill DG, Schubert J, Jia Y, Schlom DG. Determination of the thermal conductivity tensor of the n = 7 Aurivillius phase Sr4Bi4Ti7O24. Appl Phys Lett 2012;101:021904.
55. Shen XW, Fang YW, Tian BB, Duan CG. Two-dimensional ferroelectric tunnel junction: the case of monolayer in:SnSe/SnSe/Sb:SnSe homostructure. ACS Appl Electron Mater 2019;1:1133-40.
56. Chang K, Liu J, Lin H, et al. Discovery of robust in-plane ferroelectricity in atomic-thick SnTe. Science 2016;353:274-8.
57. Liu J, Chang K, JI SH, Chen X, Fu L. Apparatus and methods for memory using in-plane polarization. Available from: https://www.osti.gov/servlets/purl/1438442 [Last accessed on 11 Oct 2023].
58. Shen H, Liu J, Chang K, Fu L. In-plane ferroelectric tunnel junction. Phys Rev Appl 2019;11:024048.
Cite This Article
Export citation file: BibTeX | RIS
OAE Style
Keeney L, Colfer L, Dutta D, Schmidt M, Wei G. What lies beneath? Investigations of atomic force microscopy-based nano-machining to reveal sub-surface ferroelectric domain configurations in ultrathin films. Microstructures 2023;3:2023041. http://dx.doi.org/10.20517/microstructures.2023.41
AMA Style
Keeney L, Colfer L, Dutta D, Schmidt M, Wei G. What lies beneath? Investigations of atomic force microscopy-based nano-machining to reveal sub-surface ferroelectric domain configurations in ultrathin films. Microstructures. 2023; 3(4): 2023041. http://dx.doi.org/10.20517/microstructures.2023.41
Chicago/Turabian Style
Keeney, Lynette, Louise Colfer, Debismita Dutta, Michael Schmidt, Guannan Wei. 2023. "What lies beneath? Investigations of atomic force microscopy-based nano-machining to reveal sub-surface ferroelectric domain configurations in ultrathin films" Microstructures. 3, no.4: 2023041. http://dx.doi.org/10.20517/microstructures.2023.41
ACS Style
Keeney, L.; Colfer L.; Dutta D.; Schmidt M.; Wei G. What lies beneath? Investigations of atomic force microscopy-based nano-machining to reveal sub-surface ferroelectric domain configurations in ultrathin films. Microstructures. 2023, 3, 2023041. http://dx.doi.org/10.20517/microstructures.2023.41
About This Article
Special Issue
Copyright
Data & Comments
Data
0
Cite This Article 19 clicks
Like This Article 6
likes
Comments
Comments must be written in English. Spam, offensive content, impersonation, and private information will not be permitted. If any comment is reported and identified as inappropriate content by OAE staff, the comment will be removed without notice. If you have any queries or need any help, please contact us at support@oaepublish.com.