Abstract

This article presents a vision for advancing the development of next-generation flame-retardant materials through the utilization of metal-organic frameworks (MOFs). The proposed vision is centered on four key areas: industrialization, multifunctionality, ligand synthesis, and derivatives. By optimizing production processes, customizing MOFs for specific properties and applications, and developing novel ligands and derivatives, the effectiveness and versatility of MOFs as flame-retardant materials can be significantly enhanced. This vision represents a promising direction for the field that has the potential to address critical safety concerns across various industries.

Keywords

Microstructures, metal-organic frameworks, multifunction, industrialization, flame retardant

INTRODUCTION

Metal-organic frameworks (MOFs) are a type of porous material composed of metal ions or clusters linked by organic ligands. Their development can be traced back to the 1990s when researchers were exploring novel approaches for synthesizing materials with large surface areas and high porosity. The initial MOF structure, designated as MOF-5, was synthesized in 1999 by researchers at the University of Michigan. This material comprised Zn2+ ions coordinated with 1,4-benzenedicarboxylate (H2BDC) ligands and exhibited a remarkable surface area exceeding 2,900 m2/g[1]. In 2013, MOFs were introduced as fillers into the polymer matrix for the first time, thereby enhancing low-humidity proton conductivity[2]. This breakthrough sparked a surge of interest in MOFs, prompting researchers to explore their potential for diverse applications such as gas storage, catalysis, and drug delivery. Since then, thousands of MOFs have been synthesized using various metal ions and ligands to create materials with distinct properties and functions. MOFs have garnered attention as potential flame retardants due to their high surface area, tunable pore size, thermal stability, abundance of transition metals, and flexible structure.

The application of MOFs as flame retardants can be traced back to research conducted in the late 2010s. In 2017, Hou et al. successfully synthesized iron-based and cobalt-based MOFs, which were subsequently incorporated into PS as flame retardants. The results demonstrated a significant improvement in both the thermostability and flame retardancy of the PS composites[3]. Subsequently, researchers have investigated diverse categories of MOFs for their flame-retardant properties[3-10]. Table 1 summarizes some MOF flame retardants for different polymer matrices[11-23]. Recently, (zeolite imidazolate framework) ZIF series of MOFs have been intensively explored as potential flame retardants in various polymer matrices due to their ease of synthesis. MOFs contain flammable organic ligands in their structures, leading to limited efficiency, and therefore, modification or co-blending with other flame retardants is often required to boost their fire-retardant efficiency, e.g., performing better in UL-94 testing, especially at lower loading levels. It is accepted that MOFs usually reduce heat release rates and slow the combustion process of polymers via catalytic carbonization of transition metals within MOFs during combustion. However, there remain some unknowns on the impacts of structural compositions of MOFs on their catalyzing carbonization and modes of action. Additionally, they have explored the potential of incorporating MOFs as additives into existing flame-retardant materials to enhance their efficacy [Figure 1]. The use of MOFs as flame retardants is a relatively new and emerging area of research, and there are still ongoing debates regarding their cost-effectiveness compared to traditional flame retardants.

Metal-organic frameworks as promising flame retardants for polymeric materials

Figure 1. Data obtained with the keywords “MOF flame retard” or “MOF fire safety” in the Web of Science on August 14, 2023.

Table 1

MOF-based flame retardants for different polymer matrices

Type of MOFsAdding amount (%)MatrixUL-94LOI (%)pHRR reduction (%)Reference
ZIF-81.0PLAV-226.0- [4]
UiO-665.0PS-21.026.8 [5]
ZIF-80.91PUF-18.850.6 [6]
Zr-MOF@CeHPP2.0PCV-027.645.4 [11]
ZIF-672.0EP-23.628.7 [12]
Ni-MOF1.7 + 3.3 APPPLAV-031.026.9 [13]
ZIF-83 + 27 DDGSPPV-225.0- [14]
Fe-MOF2.0EP--18.6 [15]
Co-MOF1.5 + 4.5 APPTPUV-028.281.1 [16]
ZIF-1112.0PUF21.3 [17]
ZIF-80.75 + 2.25 EGPUEV-130.283.5 [18]
BP@MIL-531.0PCV-030.549.3 [19]
MIL-88B1.0PETV-227.023.0 [20]
TEP@MIL-533.0PS--24.7 [21]
ZIF-8/RGO2.0EPV-126.849.66 [22]
Zr-MOF4.0PCV-028.247.4 [23]

However, MOFs have several advantages over traditional flame retardants, such as their high porosity, high surface area, and tunable properties. These properties allow MOFs to be tailored to specific applications and offer superior flame-retardant performance. While MOFs may be relatively expensive compared to traditional flame retardants, their unique properties and superior flame-retardant performance may outweigh these costs in certain applications. The flame retardancy of MOFs is attributed to two primary mechanisms: gas-phase and condensed-phase. The gas-phase mechanism involves the liberation of non-flammable gases, such as water, carbon dioxide, and nitrogen. These gases can dilute the flammable gases and reduce the concentration of fuel and oxidizer in the flame zone[24,25]. The condensed-phase mechanism involves the formation of a protective layer on the surface of the polymer, which acts as a physical barrier and reduces the combustion rate. This protective layer is formed by thermal decomposition of MOFs, releasing metal oxides or metal phosphates that react with the polymer to form a char layer. The char layer functions as an insulating layer, reducing heat transfer between flame and polymer and preventing fire spread[26-29].

One may consider the potential benefits of utilizing MOFs as flame retardants, such as their capacity to enhance fire safety without adversely affecting the properties of the applied material. However, there are still some challenges associated with large-scale production and application of MOFs as flame retardants, as well as potential risks that come with using these materials. In this review, we aim to provide valuable guidance for researchers in this field by sharing our insights. One crucial aspect of MOFs is their adjustable structure, which enables precise manipulation of their physical and chemical properties. Ligand synthesis plays a pivotal role in fine-tuning the properties of MOFs, as ligands act as organic linkers that connect metal nodes and determine the framework structure. Therefore, the development of novel ligands and derivatives is imperative to enhance the versatility and performance of MOFs.

Furthermore, the industrialization of MOFs represents a crucial milestone toward their widespread commercial utilization. This entails scaling up the synthesis of MOFs, optimizing their properties for specific applications, and devising cost-effective production methods. Finally, the multifunctionality of MOFs is a key advantage that renders them suitable for a diverse range of applications. MOFs can be tailored to exhibit specific properties, such as antibacterial activity, gas storage capacity, and selective adsorption.

The future of MOFs holds immense potential for innovation and impact across various industries. To advance the field of next-generation flame-retardant materials, we present a concise vision for industrialization, versatility, ligand synthesis, and MOF derivatives. This perspective is both timely and forward-looking, offering new insights and inspiration for senior researchers, deepening the understanding of young researchers, and providing guidance for those in related fields interested in the development of flame-retardant materials. Our work aims to provide valuable insights for a wide range of researchers and facilitate future advancements in this crucial field. We are confident that our article will make a significant contribution to the ongoing efforts toward developing safer and more sustainable materials for diverse applications.

INDUSTRIAL APPLICATION OF MOF-BASED FLAME RETARDANTS

Larger scale synthesis of MOF-based flame retardants

MOFs are typically synthesized in small quantities in a laboratory setting due to the intricate nature of their synthesis. For instance, the UIO and MIL series of MOFs necessitate a hydrothermal synthesis process followed by a high-temperature reaction in a reaction vessel[30,31]. Achieving the desired MOF structure and properties requires meticulous control of reaction conditions, including temperature, pressure, and solvent composition. This process requires a significant amount of time. Even zeolite imidazolate skeleton materials (ZIFs), synthesized by facile methods, necessitate prolonged aging for the attainment of a flawless crystal structure[32,33]. The aging process is essential for the formation of intermolecular hydrogen bonds between metal ions and ligands, which stabilize the MOF structure and prevent collapse. The duration of aging can vary from several hours to several days, depending on the specific MOF being synthesized and the desired crystal quality.

To achieve commercial viability, MOFs must be produced on a large scale [Table 2]. Despite the challenges associated with their synthesis, recent advances in synthetic methods have facilitated industrial production of MOFs, enabling scaling up to gram or even kilogram quantities [Figure 2]. Continuous-flow reactors are a commonly employed strategy for the large-scale synthesis of MOFs[34-36]. In this approach, the reactants are continuously fed into the reactor and undergo controlled mixing and reaction, resulting in a steady-state production of MOFs. This method offers several benefits, including precise regulation of reaction parameters, rapid mixing, heat transfer, and continuous product output. A further approach is to employ the techniques of spray-drying or freeze-drying[37-39]. The spray-drying technique involves the atomization of a liquid MOF precursor into small droplets, which are subsequently dried using a stream of hot air. As these droplets traverse through the drying chamber, the solvent evaporates, leaving behind solid MOF particles. The method is highly efficient in the production of MOF powders and can be readily scaled up for large-scale manufacturing.

Metal-organic frameworks as promising flame retardants for polymeric materials

Figure 2. Industrial application of MOF-based flame retardants.

Table 2

Industrial methods of MOF-based flame retardants

MethodDescriptionExample applications
Continuous flow reactorsMOFs are synthesized in a continuous flow system, where reactants are continuously pumped through a reactorLarge-scale production of MOFs
Spray-dryingA solution of MOF precursors is atomized into a hot drying gas, allowing rapid solvent evaporation and MOF formation in the form of dry powderProduction of MOF powders for various applications such as coatings and composites
Freeze-dryingMOF precursors are dissolved in a solvent, frozen, and then subjected to a vacuum, causing the solvent to sublime. The resulting solid is a porous MOFProduction of highly porous MOFs with preserved crystallinity

Freeze-drying involves freezing a liquid MOF precursor and subsequently eliminating the solvent under vacuum conditions. The frozen specimen is then placed in a vacuum chamber where the solvent sublimates directly from the solid to the gas phase, resulting in a desiccated MOF powder. Freeze-drying is a more time-consuming process compared to spray-drying; however, it has the ability to maintain the crystalline structure of MOFs intact, which can prove crucial for certain applications. Both methods are capable of producing MOFs with high surface area, porosity, and thermal stability, rendering them highly versatile for a wide range of applications. Additionally, they facilitate the production of MOFs in powder form, which is more manageable and storable. Apart from that, the cost of MOFs can significantly affect large-scale production. Generally, the higher the cost of ligands, the greater the expense of producing MOFs. The price of MOF ligands can be influenced by a range of factors, such as the availability of raw materials used for synthesizing the ligands, the complexity involved in their synthesis, and the demand for MOF materials across various industries. With the advancement of novel and more efficient synthesis techniques, there is a possibility for a reduction in the cost of MOF ligands. As scientists have gained an enhanced comprehension of the structure and characteristics of MOFs, they have been able to optimize the production process of organic ligands that are utilized in creating these materials[40,41]. This has resulted in more efficient and cost-effective approaches to synthesizing MOF ligands, thereby contributing to a reduction in their price. By reducing costs through economical synthesis and purification methods, MOFs can become more competitive with other materials, leading to increased adoption in industrial applications.

Combination of MOFs with other flame retardants

In this context, the commercial potential of incorporating MOFs as flame retardants into polymers has been demonstrated due to the decreasing cost of synthetic organic ligands. Recent unpublished work and conference papers have reported on MOFs acting as synergists with traditional flame retardants [Table 3]. MOFs can be added to other flame-retardant materials to enhance their performance[18,42-48].

Table 3

Combination of MOFs with other flame retardants

MOFOther flame retardantsExample applications
Ni-MOF[13]Ammonium polyphosphateFlame-retardant additives for polymers and textiles
MOF-Cu[44]Ammonium polyphosphateFlame-retardant additives for plastics and textiles
ZIF-67[46]Ammonium polyphosphateFlame-retardant coatings and polymer formulations
ZIF-8[47]Phosphorus-based flame retardantsFlame-retardant coatings, textiles, and polymer matrices
UiO-66[48]CyclotriphosphazeneFlame-retardant composites and polymer formulations

For example, MOFs can be added to intumescent coatings, which expand when exposed to heat, forming a protective layer that insulates the underlying material and delays its ignition. The thermal stability of the expanded coatings can be improved by adding MOFs; the coking property can be increased by transition metal catalysis, and the flame-retardant property can be enhanced. Shen et al. investigated the use of MOFs as a synergist for intumescent flame retardants in polypropylene (PP). The aim was to utilize ZIF-8 for enhancing char formation and improving fire retardancy of PP. It was discovered that the incorporation of ZIF-8 facilitated better char formation and reduced the emission of flammable gases during combustion[42]. Xu et al. employed a solvothermal method to synthesize a specific type of MOF using cobalt ions and organic ligands, resulting in a porous material with high surface area and thermal stability. Subsequently, the Co-MOF was compounded with PP after being mixed with melamine polyphosphate (MPP), which is another flame retardant. The results indicate that the incorporation of Co-MOF into MPP/PP composite significantly enhances its flame retardancy, as compared to PP alone or with only MPP. This improvement is attributed to the release of water and gases from Co-MOF upon heating, which can effectively cool and dilute flames[43]. Quan et al. explore the synergistic effects of ZIFs (ZIF-67 and ZIF-8) with different transition metals on intumescent flame-retarded PP composites[49]. Overall, MOFs have the potential to be used as a synergist for intumescent flame retardants in polymers, which could lead to the development of more effective and efficient flame-retardant materials for a wide range of applications.

Escobar-Hernandez and Quan et al. provided valuable insights into the large-scale synthesis of MOFs[50,51]. They present a promising method for the sustainable and efficient production of MOF-based polymer nanocomposites[52]. The process utilized for the production of these materials is known as reactive extrusion, which involves blending MOF particles and polymers in an extruder. During this mixing procedure, chemical reactions take place between the MOFs and polymers, leading to the formation of robust chemical bonds between both materials. The sustainability and efficiency of this manufacturing process are emphasized by researchers. Reactive extrusion was utilized to produce MOF-based polymer nanocomposites with reduced energy consumption and waste generation compared to conventional methods for similar materials. Moreover, the incorporation of MOFs in these composites enhances their sustainability as they can be easily recycled and reused.

Despite their unique properties and potential for industrial applications, there are several challenges that must be overcome before MOFs can be widely adopted in the industry. MOFs are often susceptible to degradation or collapse when exposed to environmental factors such as moisture, heat, or mechanical stress. This can limit their long-term stability and durability, which is a crucial consideration for industrial applications. The cost of MOFs can be relatively high compared to traditional materials, which can limit their adoption in certain applications. Additionally, the cost of MOF synthesis and production can vary depending on the specific MOF and the synthesis method used, which can further complicate cost considerations. Addressing these challenges will require continued research and development in the synthesis, characterization, and integration of MOFs into industrial applications.

The industrialization of MOFs may follow a trajectory similar to that of graphene, which has demonstrated unique properties and potential for various industrial applications such as electronics, energy storage, and biomedical devices since its discovery in 2004[53]. However, the slow pace of industrialization can be attributed to challenges in achieving mass production and cost-effective synthesis. Nevertheless, recent advancements in graphene research have resulted in the development of various scalable production methods, including chemical vapor deposition[54], liquid-phase exfoliation[55], and reduction of graphene oxide (GO)[56]. These methods have enabled the production of high-quality graphene in large quantities at a relatively low cost, making it possible for industries to incorporate graphene into their products. Furthermore, collaborations between academia and industry have facilitated the transfer of graphene research from the lab to the factory floor. Companies, including Samsung, Nokia, and IBM, have invested in graphene research and development, leading to the creation of new graphene-based products such as flexible displays, sensors, and batteries[57]. In addition, the EU-funded Graphene Flagship project has played a crucial role in the industrialization of graphene[58]. The project, launched in 2013, aims to accelerate the commercialization of graphene by bringing together over 150 academic and industrial partners from across Europe to develop new graphene-based technologies. Overall, the combination of advancements in research, scalable production methods, industry-academia collaborations, and funding initiatives has paved the way for the industrialization of graphene. Consequently, MOF-based products are increasingly prevalent across various industries, with expectations that MOFs will continue to play a significant role in future technology development.

MULTIFUNCTION OF MOF-BASED FLAME RETARDANTS

Due to the exorbitant cost of MOF-based flame retardants, their industrialization is still in its infancy. However, as a versatile material, it can also serve other purposes, such as wastewater adsorption, while retaining its flame-retardant properties [Figure 3]. This design has become a focal point of scholarly attention. Zhou et al. utilized MOF-derived layered double hydroxide (LDH) and 3-amino-propyl triethoxy-silane to modify hydroxylated boron nitride, resulting in polyurethane foam (PUF) composites with exceptional thermal stability, fire safety, and high absorption capacity. The incorporation of flame retardants significantly decreased the amount of combustible gas and toxic CO gas generated during PUF pyrolysis. The inhibition of smoke release was evidenced by a significant decrease in the emission of aromatic compounds. Moreover, the incorporation of 1 wt.% additive resulted in PUF composites with excellent pump oil adsorption capacity, achieving a removal rate of as high as 95%, which outperformed other PUF-based materials for oil and water separation[59]. Piao et al. provided a growth site for ZIF-67 by in-situ polymerization of a polydopamine film on the surface of a polyurethane sponge. Then, ZIF-67 was etched with copper nitrate to form CuCo-LDH, and a high-performance oil-water separation flame retardant polyurethane sponge was obtained. The polyurethane composites demonstrate exceptional superhydrophobicity and superlipophilicity while also enhancing thermal stability, exhibiting excellent flame retardancy, and inhibiting the generation of toxic smoke. As such, they represent a highly efficient, sustainable, and safe material for emergency treatment of oil/organic solvent spills[60].

Metal-organic frameworks as promising flame retardants for polymeric materials

Figure 3. Multifunction of MOF-based flame retardants.

Under the influence of this trend, we believe MOFs can be designed as a “one-pack” material with specific functionalities that allow them to serve multiple roles simultaneously. In the latest reports, MOFs can be functionalized with antimicrobial agents, ultraviolet (UV) stabilizers, or other additives to provide additional properties to the material. This can be particularly useful in applications where multiple properties are required, such as in the construction of buildings or in the aerospace industry. MOFs can exhibit antimicrobial activity through the release of metal ions. Besides, their high surface area and porous nature can facilitate contact between the MOFs and microorganisms, allowing for efficient antimicrobial action.

One example is the report by Zhao et al. on the synthesis of a novel antibacterial material based on silver nanoparticle-modified 2D MOF nanosheets. The authors first synthesized the MOF nanosheets using a solvothermal method and then modified them with silver nanoparticles using a simple deposition-reduction process. The resulting hybrid nanosheets exhibited excellent stability and could be easily dispersed in water. Then, they investigated the antibacterial properties of the hybrid nanosheets against Escherichia coli and Staphylococcus aureus and found that the nanosheets exhibited excellent antibacterial activity, which was significantly enhanced under near-infrared light irradiation due to the photothermal effect of the silver nanoparticles. The authors also demonstrated that the antibacterial activity of the nanosheets could be further improved by increasing the silver content[61]. This study provides a new strategy for the design and development of antibacterial materials based on 2D MOF nanosheets modified with silver nanoparticles. The use of near-infrared light to enhance the antibacterial activity of the material could have important implications for the development of new antibacterial therapies.

Another potential application of MOFs is as UV stabilizers. UV stabilizers are compounds that are added to polymers and plastics to protect them from the damaging effects of UV light, which can cause discoloration, degradation, and ultimately failure of the material. MOFs can be functionalized with UV stabilizers to improve their efficacy. Majidi et al. dispersed the GO nanoflakes in ethanol solvent and added the precursor solution of ZIF-7. The mixture was then stirred and sonicated to ensure that the ZIF-7 coated the surface of the GO nanoflakes. The resulting modified GO nanoflakes (GO-ZIF-7) were then incorporated into a polyurethane clear-coating[62]. The researchers tested the weathering resistance and UV-shielding properties of the GO-ZIF-7-modified clear-coating and compared it to unmodified clear-coatings and coatings containing unmodified GO nanoflakes. The results showed that the GO-ZIF-7 modified clear-coating had significantly improved weathering resistance and UV-shielding properties compared to the other coatings. The MOF coating on the GO nanoflakes helped to absorb UV radiation, preventing it from penetrating the clear-coating and causing damage. Additionally, the MOF coating provided a barrier against other environmental factors, further improving the longevity of the clear coating. Therefore, the functional MOFs will continue to be developed in the future. In addition to their flame-retardant properties, MOF-based flame retardants can also influence specific functionalities to everyday applications.

MOF-derived carbon materials are synthesized by heating MOFs under controlled conditions in the absence of oxygen, resulting in the removal of the organic ligands and the formation of carbon structures[63-66]. The resulting carbon materials inherit the unique properties of the original MOFs, such as high surface area, tunable pore size, and surface functionality. The prospect of MOF-derived carbon materials is significant due to their unique properties and potential applications. Some of the advantages of these materials include: (1) High surface area: MOF-derived carbon materials have a high surface area due to their porous nature, which makes them ideal for applications such as gas storage, catalysis, and energy storage; (2) Tunable properties: By controlling the composition and pyrolysis conditions, the properties of the MOF-derived carbon materials can be tuned to meet specific application requirements; (3) Low cost: MOF-derived carbon materials can be synthesized from abundant and inexpensive precursors, making them cost-effective alternatives to other carbon materials and (4) Versatility: MOF-derived carbon materials can be synthesized in various forms, including powders, fibers, films, and monoliths, which makes them suitable for a wide range of applications.

In summary, the prospects for the multifunctionality of MOFs are very promising. Their unique properties make them highly versatile materials that can be tailored for a wide range of applications. We expect that future MOF-based flame retardants can show their functions in more aspects while ensuring fire safety. As research in this field continues, we can expect to see even more exciting applications of MOFs in the years to come.

LIGAND DESIGN OF MOF-BASED FLAME RETARDANTS

Traditional MOFs typically lack flame retardant properties due to the flammability of their organic components and the absence of other inherent flame-retardant elements, except for transition metals in metal frameworks. However, researchers have started to try to improve the flame-retardant properties of MOFs by different methods [Figure 4]. A commonly employed strategy involves the functionalization of ligand precursors with flame retardant moieties, such as phosphorus or nitrogen-containing groups, prior to their utilization in MOF synthesis[67,68]. Phosphorus is an effective flame retardant because it can capture reactive radicals upon heating, which can dilute and quench the flame. Phosphorus-containing ligands, such as phosphonic acid and phosphonate derivatives, can act as flame retardant additives by releasing phosphoric acid and other phosphorus-containing species upon thermal decomposition, which promotes the formation of an expanded carbon layer. To achieve this, phosphonate or phosphonate groups can be incorporated into the organic linkers used to construct the MOF. In addition, transition metal ions that can coordinate with phosphorus-containing ligands can be used to enhance the flame-retardant properties of the MOF. Lu et al. synthesized an organic ligand containing P/N and combined it with Co to form a novel P-MOF[69]. The researchers found that adding the P/N-treated cobalt MOFs to the lignin-based epoxy resins (EP) significantly improved their flame retardancy, as demonstrated by reduced peak heat release rates and decreased total heat release.

Metal-organic frameworks as promising flame retardants for polymeric materials

Figure 4. Ligand design of MOF-based flame retardants.

Bio-functional MOFs (Bio-MOFs) are biocompatible and biodegradable porous materials made from organic and inorganic building blocks with tunable porosity and high surface area. They can be functionalized with biological molecules to enhance selectivity and specificity, making them useful in biotechnology and environmental science[70]. Nabipour et al. used adenine as an efficient adsorbent for in situ removal of zinc ions, resulting in the formation of a bio-MOF. The as-prepared bio-MOF was then added to the EP matrix to investigate its impact on the thermal stability, smoke suppression, and flame retardancy of the EP composites. The results showed that the addition of a boom improved the flame retardancy and smoke suppression properties of the EP composites[71]. Zhou et al. present a study on a sustainable approach for simultaneously achieving flame retardancy, UV protection, and reinforcement in polylactic acid (PLA) composites using fully bio-based complexing couples. The authors used two bio-based complexing couples, tannin acid/ferric salt (TAFe) and chitosan/phytic acid (CTSPA), to fabricate the composites. The thermal and burning properties of the composites were evaluated by various tests, including TGA, limiting oxygen index (LOI), UL-94 test, and cone calorimetry. The results showed that the composites with TAFe and CTSPA had an earlier mass loss and higher char residue than pristine PLA. CTSPA also enhanced the LOI value of PLA from 19.6% to 30.5%. The study demonstrates a promising approach for developing sustainable composite materials with multiple desirable properties[72].

Harmlessness to the human body and environment-friendly recycling have become the prerequisites for the future development of flame retardants. Traditional flame retardants, such as halogenated compounds, have been found to be detrimental to both human health and the environment. Phosphorous flame retardants are commonly utilized in a diverse range of consumer goods, such as electronics, furniture, and construction materials, to mitigate the risk of fire. Nevertheless, these compounds have been associated with various potential hazards: (1) Phosphorus-based flame retardants have been found to accumulate in the environment, including soil, water, and air samples. They can also bioaccumulate in aquatic organisms and pose a toxic threat to fish and other wildlife; (2) Evidence suggests that exposure to certain phosphorus-based flame retardants may negatively impact human health. Therefore, developing effective ligands without the use of phosphorus or halogen presents a significant challenge. Overall, the utilization of biofunctional MOFs as flame retardants presents a promising avenue for research that could result in the development of safer and more environmentally sustainable materials. However, further investigation is necessary to comprehensively comprehend the properties and potential applications of these materials.

MOF DERIVATIVES TREATMENT AS FLAME RETARDANTS

As previously mentioned, the flammability of MOF ligands is a limiting factor in their inherent flame-retardant properties. Therefore, post-treatment techniques are often required to enhance their fire-resistant capabilities [Figure 5].

Metal-organic frameworks as promising flame retardants for polymeric materials

Figure 5. MOF derivatives treatment as flame retardants.

One common post-processing technique for MOFs involves the modification or removal of organic ligands. In MOFs, ligand removal can be achieved through an acid-base reaction between the MOF and solvent, which entails protonation of the organic ligand by a strong acid followed by detachment from the metal center. Generally, metal ions or clusters are linked by organic ligands in MOFs. These ligands usually contain carboxylic or amino functional groups that can serve as proton acceptors or donors, respectively. When a MOF is exposed to an acidic solution, the protons in the acid can interact with the functional groups on the ligands, resulting in protonation of the ligand. Subsequently, weakened affinity for metal centers allows easy detachment from metal ions or clusters. The liberated metal sites are then available for re-coordination with other ligands or functional groups, leading to a new MOF with altered properties[73]. The acid-base theory of ligand removal in MOFs has found diverse applications, ranging from the synthesis of novel MOFs to the functionalization of existing ones with guest molecules and the recovery of metals from them[74-76]. The judicious selection of acids and solvents can significantly impact both the extent and selectivity of ligand removal, rendering this approach highly versatile and tunable.

Previously, Pan's group have done a series of work to derive LDH by etching ZIF [Figure 6][77-82]. We incorporated mesoporous zinc hydroxystannate (ZHS) nanoparticles into NiCo-LDH nanocages that were derived from ZIF-67. The resulting composite material was then tested for its flame retardancy properties, and it was found that the LOI value of an epoxy composite containing 6 wt.% of these fillers increased to 27.2%. This improvement was significant enough to meet the UL-94 V-0 level, which is a widely recognized standard for flame retardancy. Subsequently, polyphosphazenes (PZS) is often used in modification and compounding of flame retardants because of its rich phosphorus and nitrogen, ZIF@LDH@PZS core-shell structures and LDH@PZS@NH trishell structures were synthesized through surface polycondensation on ZIF-67 using PZS, followed by ligand etching via nickel brine acidification. The interface of LDH was analyzed by adjusting the reaction time to enhance compatibility with the resin matrix. Recently, we have synthesized several hollow LDH nanocages with high thermal stability, featuring single-yolk shell nanostructures (s-CBC@LDH) and multi-yolk shell nanostructures (m-CBC@LDH). By incorporating phosphorus-based flame retardants, we have further enhanced their flame-retardant properties.

Metal-organic frameworks as promising flame retardants for polymeric materials

Figure 6. Microstructures of (A) ZHS@NCH (Reproduced with permission[77]. Copyright 2019, American Chemical Society); (B) ZIF@LDH@PZS (Reproduced with permission[78]. Copyright 2022, American Chemical Society); (C) m-CBC-P@LDH (Reproduced with permission[79]. Copyright 2023, Elsevier); (D) m-CBC@LDH (Reproduced with permission[80]. Copyright 2023, Elsevie); (E) MPOFs (Reproduced with permission[81]. Copyright 2022, American Chemical Society); (F) ZNs-B/CP (Reproduced with permission[82]. Copyright 2022, Elsevier).

In the context of flame retardancy, LDHs are often used as additives to reduce the flammability of polymers. When LDHs are added to a polymer, they act as a physical barrier that prevents the diffusion of oxygen and other flammable gases to the surface of the material, thereby reducing the rate of combustion. One issue with the physical barrier effect of LDHs is that the thickness and width of the barrier layer are limited by the amount of the LDH that can be added to the polymer matrix without affecting its properties. Thicker barriers may be required to achieve adequate flame retardancy in some applications, but a small length-diameter ratio of LDH may not meet the flame-retardant demand. One of the main challenges in using LDHs as pure inorganic flame retardants is achieving proper dispersion in the polymer matrix. Inadequate dispersion can lead to the formation of voids or weak points in the barrier layer, which can compromise its effectiveness in preventing flame spread. Therefore, to enhance the compatibility of LDH, it is typically necessary to further modify or combine it with other flame retardants. Wang et al. modified LDH by toluene diisocyanate, 2-hydroxyethyl acrylate, and vinyl triethoxysilane (LDH-TDI-HEA-VTES) to improve its compatibility with organic matrix, resulting in better dispersion of modified LDH in matrix compared with LDH[83]. The experimental results showed that with the increase of LDH-TDI-HEA-VTES content, the thermal stability, mechanical properties, flame retardant properties, and shear resistance of LDH-TDI-HEA-VTES-Acrylate composites were improved.

Moreover, acid etching can be employed to generate a novel ligand that substitutes the initial one. Wang et al. used a modified version of core-shell ZIF-67@ZIF-8, where phytic acid was added to the structure[84]. The new phytate-metal ion hybrids are formed to improve the flame retardancy of EP. Our group also utilized carboxyl POSS to modify ZIF-67 and successfully synthesized Metal-POSS Organic Frameworks (MPOFs). Thioglycolic acid was employed to replace the original imidazole ligand and complex with metal ions. Additionally, We have synthesized hollow nanocage structures with a greater number of active sites by utilizing ZIF as a sacrificial template and employing stepwise etching in the sequence of phytic acid and boric acid. Another technique is thermal treatment. This involves exposing the MOF to high temperatures, which can cause structural changes that improve their ability to act as flame retardants. Hou et al. developed a method that involves utilizing HKUST-1, a MOF, as a sacrificial template to synthesize Oxygen-Rich Covalent C2N (CNO) nanosheets through thermal treatment and chemical vapor deposition[85].

In summary, conventional MOF ligands are often composed of organic compounds that possess flammability. Additionally, the limited presence of flame-retardant elements in MOFs may result in reduced flame-retardant effects and decreased practicality. The method of post-treatment MOFs is simple and controllable and has the following advantages: (1) Endowing MOFs with more flame-retardant elements: by incorporating additional flame-retardant elements, such as phosphorus or nitrogen, into the MOF structure during post-treatment, their flame retardancy can be enhanced; (2) This method involves breaking the coordination bonds between the metal ions and the ligands in the MOF, which allows for the creation of a hybrid material that inherits some desirable properties of the original MOF, while also introducing new features; (3) Generating expanded pores: post-treatment of MOFs can create larger pores or expand existing ones, which can improve their ability to adsorb volatile organic compounds and harmful gases produced during polymer combustion. The expanded pores can be used as a carrier to load phosphorus-based flame retardants, which can further improve the flame retardancy of MOFs. Zhao et al. transformed the microporous structure of MIL-53 into macropores via ammonia water treatment under closed conditions, thereby enhancing its specific surface area and adsorption capacity[21]. The excellent porous architecture was then utilized for triethyl phosphate (TEP) adsorption as a flame retardant in polystyrene and (4) Controlling morphology: multi-level pore structures can provide more active sites for catalytic reactions. Hollow structures can reduce the weight of flame retardants, which can improve their dispersion and increase the number of active sites available for flame retardancy. As a result, the flame-retardant efficiency has been significantly enhanced while minimizing any adverse effects on the mechanical properties of EP composites.

OUTLOOK

This perspective provides a concise overview of the latest research advances in MOF flame retardants and offers insights into their prospects. Compared to other commonly used fillers, such as platelet-like clay, carbon-based fillers, and silicates, MOFs offer several distinct advantages: In Gas-Phase, Certain MOFs containing nitrogen or phosphorus-containing organic ligands exhibit gas-phase action, effectively trapping active radicals and diluting combustible gases. This gas-phase action contributes to the overall flame retardancy of polymers by interrupting the combustion chain and reducing the availability of flammable gases. In the condensed phase, the metal ions or clusters present in MOFs act as catalytic centers, promoting char formation during combustion. This catalytic activity enhances the formation of a protective char layer, which acts as a barrier against heat and mass transfer, thereby improving the flame retardancy of the polymer. Furthermore, MOFs offer a high degree of tunability, allowing for the customization of their properties to suit specific applications. The pore size, surface area, and composition of MOFs can be tailored to optimize flame retardant performance and address specific requirements of the polymer matrix. These advantages position MOFs as promising alternatives to conventional flame-retardant fillers.

The cost outlook of MOF flame retardants is an important consideration for their widespread adoption in various industries. The cost of MOF flame retardants is influenced by several factors, including the cost of raw materials, the synthesis process, and the scale of production. One approach to reducing their cost is to optimize the synthesis process. The development of more efficient and scalable synthesis methods can reduce the cost of production and increase the yield of MOFs. Additionally, the use of cheaper starting materials and reagents can also lower the cost of MOF flame retardants. Another approach to improving the cost-effectiveness of MOF flame retardants is to increase their functionality and versatility. By designing MOFs with multiple functions, their value proposition can be increased, which can justify the higher cost. In addition to industrialization, researchers are also striving to develop multifunctional MOFs that can perform multiple tasks simultaneously. These types of MOFs can be engineered not only for flame retardants but also for gas absorption, antibacterial activity, or pollutant filtration. Ligand synthesis and derivatives are also important areas of research in the development of MOFs for flame retardant applications. By designing novel ligands and derivatives, researchers can precisely adjust the properties of MOFs to enhance their efficacy in fire suppression. Altering the structure of ligands or introducing new functional groups can elevate the thermal stability or augment the flame-retardant characteristics of MOFs.

The potential of MOFs in the field of flame retardancy is promising, with ongoing research expected to yield more effective and widely applicable flame-retardant materials that can address important safety concerns across a multitude of industries.

DECLARATIONS

Authors’ contributions

Conceptual design and project supervision: Pan YT

Manuscript draft and revision: Song P, Hou B

Availability of data and materials

Not applicable.

Financial support and sponsorship

This work was supported by the National Natural Science Foundation of China (No.22005029) and the Australian Research Council (FT190100188; LP220100278).

Ethical approval and consent to participate

Not applicable.

Conflicts of interest

All authors declared that there are no conflicts of interest.

Consent for publication

Not applicable.

Copyright

© The Author(s) 2023.

REFERENCES

1. Li H, Eddaoudi M, O'keeffe M, Yaghi OM. Design and synthesis of an exceptionally stable and highly porous metal-organic framework. Nature 1999;402:276-9.

2. Huo J, Marcello M, Garai A, Bradshaw D. MOF-polymer composite microcapsules derived from Pickering emulsions. Adv Mater 2013;25:2717-22.

3. Hou Y, Hu W, Gui Z, Hu Y. Preparation of metal-organic frameworks and their application as flame retardants for polystyrene. Ind Eng Chem Res 2017;56:2036-45.

4. Shi X, Dai X, Cao Y, Li J, Huo C, Wang X. Degradable poly(lactic acid)/metal-organic framework nanocomposites exhibiting good mechanical, flame retardant, and dielectric properties for the fabrication of disposable electronics. Ind Eng Chem Res 2017;56:3887-94.

5. Chen W, Jiang Y, Qiu R, Xu W, Hou Y. Investigation of UiO-66 as flame retardant and its application in improving fire safety of polystyrene. Macromol Res 2020;28:42-50.

6. Zhao S, Yin L, Zhou Q, Liu C, Zhou K. In situ self-assembly of zeolitic imidazolate frameworks on the surface of flexible polyurethane foam: towards for highly efficient oil spill cleanup and fire safety. Appl Surf Sci 2020;506:144700.

7. Wang M, Song X, Jiang J, Xia J, Li M. Influence of zeolitic imidazolate framework-8 on the thermal stabilization of poly(vinyl chloride). Polym Degrad Stab 2018;149:112-8.

8. Nabipour H, Nie S, Wang X, Song L, Hu Y. Highly flame retardant zeolitic imidazole framework-8@cellulose composite aerogels as absorption materials for organic pollutants. Cellulose 2020;27:2237-51.

9. Nabipour H, Nie S, Wang X, Song L, Hu Y. Zeolitic imidazolate framework-8/polyvinyl alcohol hybrid aerogels with excellent flame retardancy. Compos A Appl Sci Manuf 2020;129:105720.

10. Seidi F, Jouyandeh M, Taghizadeh M, et al. Metal-organic framework (MOF)/epoxy coatings: a review. Materials 2020;13:2881.

11. Sai T, Ran S, Guo Z, et al. Deposition growth of Zr-based MOFs on cerium phenylphosphonate lamella towards enhanced thermal stability and fire safety of polycarbonate. Compos B Eng 2020;197:108064.

12. Li A, Xu W, Chen R, Liu Y, Li W. Fabrication of zeolitic imidazolate frameworks on layered double hydroxide nanosheets to improve the fire safety of epoxy resin. Compos A Appl Sci Manuf 2018;112:558-71.

13. Wang X, Wang S, Wang W, et al. The flammability and mechanical properties of poly (lactic acid) composites containing Ni-MOF nanosheets with polyhydroxy groups. Compos B Eng 2020;183:107568.

14. Xie J, Shi X, Zhang M, Dai X, Wang X. Improving the flame retardancy of polypropylene by nano metal-organic frameworks and bioethanol coproduct. Fire Mater 2019;43:373-80.

15. Zheng Y, Lu Y, Zhou K. A novel exploration of metal-organic frameworks in flame-retardant epoxy composites. J Therm Anal Calorim 2019;138:905-14.

16. Wang H, Qiao H, Guo J, et al. Preparation of cobalt-based metal organic framework and its application as synergistic flame retardant in thermoplastic polyurethane (TPU). Compos B Eng 2020;182:107498.

17. Cheng J, Ma D, Li S, Qu W, Wang D. Preparation of zeolitic imidazolate frameworks and their application as flame retardant and smoke suppression agent for rigid polyurethane foams. Polymers 2020;12:347.

18. Wang G, Xu W, Chen R, Li W, Liu Y, Yang K. Synergistic effect between zeolitic imidazolate framework-8 and expandable graphite to improve the flame retardancy and smoke suppression of polyurethane elastomer. J Appl Polymer Sci 2020;137:48048.

19. Qian Z, Zou B, Xiao Y, et al. Targeted modification of black phosphorus by MIL-53(Al) inspired by “Cannikin's Law” to achieve high thermal stability of flame retardant polycarbonate at ultra-low additions. Compos B Eng 2022;238:109943.

20. Ma T, Wang W, Wang R. Thermal degradation and carbonization mechanism of Fe-based metal-organic frameworks onto flame-retardant polyethylene terephthalate. Polymers 2023;15:224.

21. Zhao H, Yuan B, Zhan Y, et al. Upgrading the pore-size scale of MIL-53 from microporous to macroporous for adsorbing triethyl phosphate and reducing the fire risk of polystyrene. Compos A Appl Sci Manuf 2022;159:107003.

22. Xu B, Xu W, Wang G, Liu L, Xu J. Zeolitic imidazolate frameworks-8 modified graphene as a green flame retardant for reducing the fire risk of epoxy resin. Polym Adv Techs 2018;29:1733-43.

23. Sai T, Ran S, Guo Z, Fang Z. A Zr-based metal organic frameworks towards improving fire safety and thermal stability of polycarbonate. Compos B Eng 2019;176:107198.

24. Salmeia K, Fage J, Liang S, Gaan S. An overview of mode of action and analytical methods for evaluation of gas phase activities of flame retardants. Polymers 2015;7:504-26.

25. Molyneux S, Stec AA, Hull TR. The effect of gas phase flame retardants on fire effluent toxicity. Polym Degrad Stab 2014;106:36-46.

26. Schartel B, Perret B, Dittrich B, et al. Flame retardancy of polymers: the role of specific reactions in the condensed phase. Macromol Mater Eng 2016;301:9-35.

27. Bao C, Guo Y, Yuan B, Hu Y, Song L. Functionalized graphene oxide for fire safety applications of polymers: a combination of condensed phase flame retardant strategies. J Mater Chem 2012;22:23057-63.

28. Xu Z, Xing W, Hou Y, et al. The combustion and pyrolysis process of flame-retardant polystyrene/cobalt-based metal organic frameworks (MOF) nanocomposite. Combust Flame 2021;226:108-16.

29. Laoutid F, Bonnaud L, Alexandre M, Lopez-Cuesta JM, Dubois Ph. New prospects in flame retardant polymer materials: from fundamentals to nanocomposites. Mater Sci Eng R Rep 2009;63:100-25.

30. Ru J, Wang X, Wang F, Cui X, Du X, Lu X. UiO series of metal-organic frameworks composites as advanced sorbents for the removal of heavy metal ions: synthesis, applications and adsorption mechanism. Ecotoxicol Environ Saf 2021;208:111577.

31. Tomar S, Singh V. Review on synthesis and application of MIL-53. Mater Today Proc 2021;43:3291-6.

32. Şahin F, Topuz B, Kalıpçılar H. Synthesis of ZIF-7, ZIF-8, ZIF-67 and ZIF-L from recycled mother liquors. Microporous Mesoporous Mater 2018;261:259-67.

33. Lee Y, Jang M, Cho H, Kwon H, Kim S, Ahn W. ZIF-8: a comparison of synthesis methods. Chem Eng J 2015;271:276-80.

34. Bagi SD, Myerson AS, Román-leshkov Y. Solvothermal crystallization kinetics and control of crystal size distribution of MOF-808 in a continuous flow reactor. Cryst Growth Des 2021;21:6529-36.

35. Batten MP, Rubio-martinez M, Hadley T, et al. Continuous flow production of metal-organic frameworks. Curr Opin Chem Eng 2015;8:55-9.

36. Dunne PW, Lester E, Walton RI. Towards scalable and controlled synthesis of metal-organic framework materials using continuous flow reactors. React Chem Eng 2016;1:352-60.

37. Amery N, Abid H, Al-saadi S, Wang S, Liu S. Facile directions for synthesis, modification and activation of MOFs. Mater Today Chem 2020;17:100343.

38. Liu X, Xie L, Wu Y. Recent advances in the shaping of metal-organic frameworks. Inorg Chem Front 2020;7:2840-66.

39. Rubio-Martinez M, Avci-Camur C, Thornton AW, Imaz I, Maspoch D, Hill MR. New synthetic routes towards MOF production at scale. Chem Soc Rev 2017;46:3453-80.

40. Bagi S, Yuan S, Rojas-buzo S, Shao-horn Y, Román-leshkov Y. A continuous flow chemistry approach for the ultrafast and low-cost synthesis of MOF-808. Green Chem 2021;23:9982-91.

41. Kochetygov I, Roth J, Espín J, et al. A simple, transition metal catalyst-free method for the design of complex organic building blocks used to construct porous metal-organic frameworks. Angew Chem Int Ed Eng 2023;62:e202215595.

42. Shen R, Quan Y, Zhang Z, Ma R, Wang Q. Metal-organic framework as an efficient synergist for intumescent flame retardants against highly flammable polypropylene. Ind Eng Chem Res 2022;61:7292-302.

43. Xu Y, Zhou R, Ma G, et al. Preparation of a cobalt metal-organic framework (Co-MOF) and its application as a polypropylene flame retardant by compounding with melamine polyphosphate. Polym Test 2022;116:107765.

44. Chen X, Chen X, Li S, Jiao C. Copper metal-organic framework toward flame-retardant enhancement of thermoplastic polyurethane elastomer composites based on ammonium polyphosphate. Polym Adv Technol 2021;32:2829-42.

45. Li H, Meng D, Qi P, et al. Fabrication of a hybrid from metal organic framework and sepiolite (ZIF-8@SEP) for reducing the fire hazards in thermoplastic polyurethane. Appl Clay Sci 2022;216:106376.

46. Liu Q, Wang H, Li H, Sun J, Gu X, Zhang S. Constructing a novel synergistic flame retardant by hybridization of zeolitic imidazolate framework-67 and graphene oxide for thermoplastic polyurethane. Poly Adv Technol 2022;33:2374-85.

47. Yue Z, Lin J, Yang D, et al. In situ growth of nano-MOFs on ammonium polyphosphate particles for boosting flame retardancy, smoke suppression and mechanical properties of epoxy. J Mater Sci 2022;57:20082-94.

48. Jiang J, Huo S, Zheng Y, et al. A novel synergistic flame retardant of hexaphenoxycyclotriphosphazene for epoxy resin. Polymers 2021;13:3648.

49. Quan Y, Shen R, Schweizer C, et al. Synergistic effects of zeolitic imidazolate frameworks (ZIFs) with different transition metals on intumescent flame-retarded polypropylene composites: a comparative study. J Mater Sci Technol 2023;155:102-10.

50. Escobar-hernandez HU, Shen R, Papadaki MI, Powell JA, Zhou H, Wang Q. Hazard evaluation of metal-organic framework synthesis and scale-up: a laboratory safety perspective. ACS Chem Health Saf 2021;28:358-68.

51. Quan Y, Parker TF, Hua Y, Jeong H, Wang Q. Process elucidation and hazard analysis of the metal-organic framework scale-up synthesis: a case study of ZIF-8. Ind Eng Chem Res 2023;62:5035-41.

52. Quan Y, Shen R, Ma R, Zhang Z, Wang Q. Sustainable and efficient manufacturing of metal-organic framework-based polymer nanocomposites by reactive extrusion. ACS Sustain Chem Eng 2022;10:7216-22.

53. Novoselov KS, Geim AK, Morozov SV, et al. Electric field effect in atomically thin carbon films. Science 2004;306:666-9.

54. Murdock AT, Koos A, Britton TB, et al. Controlling the orientation, edge geometry, and thickness of chemical vapor deposition graphene. ACS Nano 2013;7:1351-9.

55. Hernandez Y, Nicolosi V, Lotya M, et al. High-yield production of graphene by liquid-phase exfoliation of graphite. Nat Nanotechnol 2008;3:563-8.

56. Agarwal V, Zetterlund PB. Strategies for reduction of graphene oxide - a comprehensive review. Chem Eng J 2021;405:127018.

57. Zurutuza A, Marinelli C. Challenges and opportunities in graphene commercialization. Nat Nanotechnol 2014;9:730-4.

58. Milana S. The lab-to-fab journey of 2D materials. Nat Nanotechnol 2019;14:919-21.

59. Zhou Y, Qiu S, Chu F, et al. High-performance flexible polyurethane foam based on hierarchical BN@MOF-LDH@APTES structure: enhanced adsorption, mechanical and fire safety properties. J Colloid Interface Sci 2022;609:794-806.

60. Piao J, Lu M, Ren J, et al. MOF-derived LDH modified flame-retardant polyurethane sponge for high-performance oil-water separation: Interface engineering design based on bioinspiration. J Hazard Mater 2023;444:130398.

61. Zhao X, Qiu H, Shao Y, et al. Silver nanoparticle-modified 2D MOF nanosheets for photothermally enhanced silver ion release antibacterial treatment. Acta Physico Chimica Sinica 2023;39:2211043.

62. Majidi R, Keramatinia M, Ramezanzadeh B, Ramezanzadeh M. Weathering resistance (UV-shielding) improvement of a polyurethane automotive clear-coating applying metal-organic framework (MOF) modified GO nano-flakes (GO-ZIF-7). Polym Degrad Stab 2023;207:110211.

63. Wang C, Kim J, Tang J, et al. New strategies for novel MOF-derived carbon materials based on nanoarchitectures. Chem 2020;6:19-40.

64. Ren J, Huang Y, Zhu H, et al. Recent progress on MOF-derived carbon materials for energy storage. Carbon Energy 2020;2:176-202.

65. Marpaung F, Kim M, Khan JH, et al. Metal-organic framework (MOF)-derived nanoporous carbon materials. Chem Asian J 2019;14:1331-43.

66. Chaikittisilp W, Ariga K, Yamauchi Y. A new family of carbon materials: synthesis of MOF-derived nanoporous carbons and their promising applications. J Mater Chem A 2013;1:14-9.

67. Hou Y, Xu Z, Chu F, et al. A review on metal-organic hybrids as flame retardants for enhancing fire safety of polymer composites. Compos B Eng 2021;221:109014.

68. Sai T, Su Y, Shen H, et al. Fabrication and mechanism study of cerium-based P, N-containing complexes for reducing fire hazards of polycarbonate with superior thermostability and toughness. ACS Appl Mater Interfaces 2021;13:30061-75.

69. Lu X, Lee AF, Gu X. Improving the flame retardancy of sustainable lignin-based epoxy resins using phosphorus/nitrogen treated cobalt metal-organic frameworks. Mater Today Chem 2022;26:101184.

70. Zulys A, Yulia F, Muhadzib N, Nasruddin. Biological metal-organic frameworks (Bio-MOFs) for CO2 capture. Ind Eng Chem Res 2021;60:37-51.

71. Nabipour H, Qiu S, Wang X, Song L, Hu Y. Adenine as an efficient adsorbent for zinc ions removal from wastewater to in situ form bio-based metal-organic frameworks: a novel approach to preparing fire-safe polymers. Compos A Appl Sci Manuf 2022;161:107099.

72. Zhou Y, Tawiah B, Noor N, et al. A facile and sustainable approach for simultaneously flame retarded, UV protective and reinforced poly(lactic acid) composites using fully bio-based complexing couples. Compos B Eng 2021;215:108833.

73. Hamisu AM, Ariffin A, Wibowo AC. Cation exchange in metal-organic frameworks (MOFs): the hard-soft acid-base (HSAB) principle appraisal. Inorganica Chim Acta 2020;511:119801.

74. Bao S, Li J, Guan B, Jia M, Terasaki O, Yu J. A green selective water-etching approach to MOF@mesoporous SiO2 yolk-shell nanoreactors with enhanced catalytic stabilities. Matter 2020;3:498-508.

75. Lee S, Oh S, Oh M. Atypical hybrid metal-organic frameworks (MOFs): a combinative process for MOF-on-MOF growth, etching, and structure transformation. Angew Chem 2020;132:1343-9.

76. Narciso J, Ramos-fernandez EV, Delgado-marín JJ, Affolter CW, Olsbye U, Redekop EA. New route for the synthesis of Co-MOF from metal substrates. Microporous Mesoporous Mater 2021;324:111310.

77. Zhang Z, Li X, Yuan Y, Pan YT, Wang DY, Yang R. Confined dispersion of zinc hydroxystannate nanoparticles into layered bimetallic hydroxide nanocapsules and its application in flame-retardant epoxy nanocomposites. ACS Appl Mater Interfaces 2019;11:40951-60.

78. Hou B, Song K, Ur Rehman Z, et al. Precise control of a yolk-double shell metal-organic framework-based nanostructure provides enhanced fire safety for epoxy nanocomposites. ACS Appl Mater Interfaces 2022;14:14805-16.

79. Song K, Zhang H, Pan YT, et al. Metal-organic framework-derived bird's nest-like capsules for phosphorous small molecules towards flame retardant polyurea composites. J Colloid Interface Sci 2023;643:489-501.

80. Song K, Li X, Pan Y, et al. The influence on flame retardant epoxy composites by a bird’s nest-like structure of Co-based isomers evolved from zeolitic imidazolate framework-67. Polym Degrad Stab 2023;211:110318.

81. Hou B, Zhang W, Lu H, et al. Multielement flame-retardant system constructed with metal POSS-organic frameworks for epoxy resin. ACS Appl Mater Interfaces 2022;14:49326-37.

82. Song K, Hou B, Ur Rehman Z, et al. “Sloughing” of metal-organic framework retaining nanodots via step-by-step carving and its flame-retardant effect in epoxy resin. Chem Eng J 2022;448:137666.

83. Wang X, Chen Q, Zheng Y, Hong M, Fu H. Study on novel flame retarded LDH-TDI-HEA-VTES-acrylate composites and their flame retardant mechanism. React Funct Polym 2020;147:104371.

84. Wang H, Li X, Su F, et al. Core-shell ZIF67@ZIF8 modified with phytic acid as an effective flame retardant for improving the fire safety of epoxy resins. ACS Omega 2022;7:21664-74.

85. Hou Y, Chu F, Ma S, Hu Y, Hu W, Gui Z. Rapid synthesis of oxygen-rich covalent C2N (CNO) nanosheets by sacrifice of HKUST-1: advanced metal-free nanofillers for polymers. ACS Appl Mater Interfaces 2018;10:32688-97.

Cite This Article

Review
Open Access
Metal-organic frameworks as promising flame retardants for polymeric materials
Boyou Hou, ... Pingan Song

How to Cite

Hou, B.; Pan, Y. T.; Song, P. Metal-organic frameworks as promising flame retardants for polymeric materials. Microstructures. 2023, 3, 2023039. http://dx.doi.org/10.20517/microstructures.2023.37

Download Citation

If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click on download.

Export Citation File:

Type of Import

Tips on Downloading Citation

This feature enables you to download the bibliographic information (also called citation data, header data, or metadata) for the articles on our site.

Citation Manager File Format

Use the radio buttons to choose how to format the bibliographic data you're harvesting. Several citation manager formats are available, including EndNote and BibTex.

Type of Import

If you have citation management software installed on your computer your Web browser should be able to import metadata directly into your reference database.

Direct Import: When the Direct Import option is selected (the default state), a dialogue box will give you the option to Save or Open the downloaded citation data. Choosing Open will either launch your citation manager or give you a choice of applications with which to use the metadata. The Save option saves the file locally for later use.

Indirect Import: When the Indirect Import option is selected, the metadata is displayed and may be copied and pasted as needed.

About This Article

© The Author(s) 2023. Open Access This article is licensed under a Creative Commons Attribution 4.0 International License (https://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, sharing, adaptation, distribution and reproduction in any medium or format, for any purpose, even commercially, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.

Related

Open Access | Perspective | 29 May 2024
Views: 355 | Downloads: 124
Download PDF 0 4
Open Access | Review | 9 Aug 2023
Views: 1251 | Downloads: 392
Download PDF 0 4
Open Access | Perspective | 25 Apr 2023
Views: 723 | Downloads: 611
Download PDF 0 3
Open Access | Research Article | 13 Feb 2023
Views: 1107 | Downloads: 770
Download PDF 0 2
Open Access | Perspective | 15 Jun 2022
Views: 2427 | Downloads: 1359
Download PDF 0 33
Open Access | Review | 16 Jan 2022
Views: 2888 | Downloads: 1547
Download PDF 0 29
Open Access | Research Article | 12 Jan 2022
Views: 2300 | Downloads: 951
Download PDF 0 0
Open Access | Research Article | 22 Sep 2021
Views: 1899 | Downloads: 937
Download PDF 0 14
Open Access | Review | 23 Oct 2024
Views: 348 | Downloads: 155
Download PDF 0 0
Open Access | Research Article | 16 Oct 2024
Views: 383 | Downloads: 101
Download PDF 0 0

Data & Comments

Data

Views
921
Downloads
269
Citations
Comments
0
1

Comments

Comments must be written in English. Spam, offensive content, impersonation, and private information will not be permitted. If any comment is reported and identified as inappropriate content by OAE staff, the comment will be removed without notice. If you have any queries or need any help, please contact us at support@oaepublish.com.

0
Download PDF
Share This Article
Scan the QR code for reading!
See Updates
Contents
Figures
Related
Microstructures
ISSN 2770-2995 (Online)

Portico

All published articles are preserved here permanently:

https://www.portico.org/publishers/oae/

Portico

All published articles are preserved here permanently:

https://www.portico.org/publishers/oae/